Stahlgeschnittene Drahtkugeln
Steel cut wire is produced from recycled steel wires, such as bead wires and steel ropes, which are cut into granules using specialized cutting machines. This ensures consistent quality and durability for demanding blasting applications.
Compared with standard steel shots, cut wire features higher hardness, often exceeding 50 HRC. With advanced rounding processes, it can also be transformed into spherical cut shots, offering superior blasting performance and longer service life.
Produktdetails
Stahlschrot wird durch das Zerkleinern hochwertiger Stahldrähte zu gleichmäßigen Körnern hergestellt. Je nach Herstellungsverfahren ist er in zwei Hauptformen erhältlich: zylindrischer Stahlschrot und kugelförmiger Stahlschrot (abgerundeter Schrot). Durch fortschrittliche Abrundungstechnologie werden die Schnittkanten entfernt, wodurch ein glattes und langlebiges Schrotmaterial entsteht.
Merkmale
Hohe Härte – In der Regel über 50 HRC, deutlich härter als herkömmliche Stahlgusskugeln, was eine hohe Strahlleistung gewährleistet.
Robust und langlebig – Eine gleichmäßige Mikrostruktur und eine hervorragende Ermüdungsfestigkeit sorgen für eine längere Lebensdauer.
Gleichbleibende Form – Erhältlich sowohl in zylindrischer als auch in kugelförmiger Ausführung, wodurch eine gleichbleibende Strahlqualität gewährleistet wird.
Größenbereich – Standardgrößen von CW1,0 mm bis CW3,0 mm; Sondergrößen sind auf Anfrage erhältlich.
Produktdaten
| Artikel | Spezifikation | Wert |
|---|---|---|
| Chemical Composition | Carbon (C) | 0.45 ~ 0.75% |
| Manganese (Mn) | 0.40 ~ 1.20% | |
| Silicon (Si) | 0.10 ~ 0.30% | |
| Sulfur (S) | < 0.04% | |
| Phosphorus (P) | < 0.04% | |
| Average Hardness |
1.0 mm: 51 ~ 53 HRC (525 ~ 561 HV) 1.5 mm: 41 ~ 45 HRC (388 ~ 436 HV) | |
| Hardness Deviation | Maximum deviation: ±1.0 HRC or ±40 HV | |
| Tensile Strength |
1.0 mm: 1750 ~ 2150 MPa 1.5 mm: 1250 ~ 1450 MPa | |
| Metallographic Structure | Longitudinal (uniform deformed austenite) / Transverse (uniform deformed austenite) | |
| Minimum Density (Alcohol Displacement Method) | 7.8 g/cm³ | |
Produktanwendungen
Steel cut wires are produced from national standard bead wires and are widely applied in machinery, automotive, shipbuilding, steel structure, pipeline industries, and other manufacturing sectors for surface cleaning and strengthening of workpieces. During shot blasting, the cut wire shots are propelled at high speed by the blasting machine in a parabolic trajectory, effectively removing rust and oxide layers from the product surface while achieving the required finish and surface roughness. Among the available sizes, CW1.5mm is the most commonly used, with hardness typically exceeding 50HRC.
Due to their higher hardness, usually above 50HRC, steel cut wire shots can sometimes cause scuffing on softer materials, particularly those with hardness below 48HRC. For this reason, it is often recommended to mix steel cut wire shots with steel shots or steel grits of similar size for shot blasting. In practice, some customers also mix low-carbon steel shots with steel cut wire shots, which has proven to deliver excellent blasting results.