Steel Grit
We are dedicated to producing high-quality steel grit with meticulous care and advanced processes.
All our steel grit is manufactured in accordance with SAE standards, covering GP, GL, and GH types in full size ranges from G12 to G120. Using premium raw materials and state-of-the-art techniques—such as centrifugation, tempering, double quenching, and upgraded screening—our products have gained strong recognition worldwide. In addition, we also offer customized options for size and hardness to meet specific customer needs.
Product Details
Steel grit is produced by crushing high-quality steel shot, ensuring excellent overall quality. With nearly 20 years of manufacturing experience and strong teamwork, we have continuously improved our processes to deliver higher value-added products to our customers.
We supply steel grit in a wide range of sizes, including G12, G14, G16, G18, G25, G40, G50, G80, and G120. According to different hardness levels, three types are available:
GP: 40–50 HRC
GL: 50–60 HRC
GH: 60–66 HRC
Product Specifications
| Item | Specification | Value |
|---|---|---|
| Chemical Composition | Carbon (C) | 0.70 ~ 1.20% |
| Manganese (Mn) | 0.35 ~ 1.20% | |
| Silicon (Si) | 0.40 ~ 1.20% | |
| Sulfur (S) | ≤ 0.05% | |
| Phosphorus (P) | ≤ 0.05% | |
| Average Hardness (500g Load) |
GP Steel Shot: 42 ~ 50 HRC (399 ~ 509 HV) GL Steel Shot: 56 ~ 60 HRC (620 ~ 713 HV) GH Steel Shot: 63 ~ 66 HRC (759 ~ 889 HV) | |
| Hardness Deviation | Maximum deviation: ±3.0 HRC or ±40 HV | |
| Microstructure | Uniform tempered martensite or tempered troostite with finely dispersed carbides | |
| Minimum Density (Alcohol Displacement Method) | 7.6 g/cm³ | |
| 目数 Mesh | mm | 2.5 | 2.0 | 1.7 | 1.4 | 1.2 | 1.0 | 0.7 | 0.4 | 0.3 | 0.2 |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 7 | 2.30 | all pass | |||||||||
| 8 | 2.36 | all pass | |||||||||
| 10 | 2.00 | 80%min | all pass | ||||||||
| 12 | 1.70 | 90%min | 80%min | all pass | |||||||
| 13 | 1.40 | 90%min | 80%min | all pass | |||||||
| 16 | 1.18 | 90%min | 75%min | all pass | |||||||
| 18 | 1.00 | 85%min | 75%min | all pass | |||||||
| 20 | 0.850 | ||||||||||
| 25 | 0.710 | 85%min | 70%min | all pass | |||||||
| 30 | 0.600 | ||||||||||
| 35 | 0.500 | ||||||||||
| 40 | 0.425 | 80%min | 70%min | all pass | |||||||
| 45 | 0.355 | ||||||||||
| 50 | 0.300 | 80%min | 65%min | all pass | |||||||
| 80 | 0.180 | 75%min | 65%min | ||||||||
| 120 | 0.125 | 75%min | 60%min | ||||||||
| 200 | 0.075 | 70%min | |||||||||
| 325 | 0.045 | ||||||||||
| SAE J444 | G-10 | G-12 | G-14 | G-16 | G-18 | G-25 | G-40 | G-50 | G-80 | G-120 | |
Product Applications
In shipyards, hull surfaces are treated with primary and secondary sandblasting for effective rust removal and cleaning. Similarly, the pretreatment line for hull steel plates also involves sandblasting and rust removal to ensure a clean and prepared surface.
For steel structures, section steel, steel plates, and accessories are processed by continuous shot blasting machines. This ensures the required cleanliness and surface roughness, providing an ideal foundation for subsequent processes such as painting and coating. To help customers minimize production costs and reduce abrasive consumption, we focus on supplying high-quality, cost-effective steel shots.
Applications:
Rust Removal: shot blasting, shot peening, casting rust removal, forging rust removal, steel plate rust removal, H-beam rust removal, and steel structure rust removal.
Shot Blasting: section steel, ship plates, steel plates, and other steel components.
Pretreatment: coating pretreatment, surface pretreatment, ship plate pretreatment, steel plate pretreatment, and structural steel pretreatment.