Çelik Kesimli Tel Bilye
Steel cut wire is produced from recycled steel wires, such as bead wires and steel ropes, which are cut into granules using specialized cutting machines. This ensures consistent quality and durability for demanding blasting applications.
Compared with standard steel shots, cut wire features higher hardness, often exceeding 50 HRC. With advanced rounding processes, it can also be transformed into spherical cut shots, offering superior blasting performance and longer service life.
Ürün Detayları
Çelik Kesilmiş Tel Bilye, yüksek kaliteli çelik tellerin eşit büyüklükte granüller halinde kesilmesiyle üretilir. Üretim sürecine bağlı olarak, iki ana şekilde tedarik edilebilir: silindirik kesilmiş tel ve küresel kesilmiş tel (yuvarlak bilye). Gelişmiş yuvarlama teknolojisi sayesinde kesik kenarlar ortadan kaldırılır ve pürüzsüz, dayanıklı bir bilye malzemesi elde edilir.
Özellikler
Yüksek Sertlik – Genellikle 50 HRC’nin üzerinde olup, geleneksel dökme çelik bilyelere kıyasla çok daha serttir ve yüksek performanslı kumlama sağlar.
Dayanıklı ve Uzun Ömürlü – Tekdüze mikro yapı ve mükemmel yorulma direnci, daha uzun bir kullanım ömrü sağlar.
Tutarlı Şekil – Hem silindirik hem de küresel şekillerde mevcuttur ve istikrarlı kumlama kalitesi sunar.
Boyut Aralığı – CW1,0 mm ile CW3,0 mm arası standart boyutlar; talep üzerine özel boyutlar da temin edilebilir.
Ürün Özellikleri
| Öğe | Şartname | Değer |
|---|---|---|
| Kimyasal Bileşim | Karbon (C) | 0.45 ~ 0.75% |
| Manganez (Mn) | 0.40 ~ 1.20% | |
| Silikon (Si) | 0.10 ~ 0.30% | |
| Kükürt (S) | < 0.04% | |
| Fosfor (P) | < 0.04% | |
| Ortalama Sertlik |
1.0 mm: 51 ~ 53 HRC (525 ~ 561 HV) 1.5 mm: 41 ~ 45 HRC (388 ~ 436 HV) | |
| Sertlik Sapması | Maximum deviation: ±1.0 HRC or ±40 HV | |
| Tensile Strength |
1.0 mm: 1750 ~ 2150 MPa 1.5 mm: 1250 ~ 1450 MPa | |
| Metallografik Yapı | Longitudinal (uniform deformed austenite) / Transverse (uniform deformed austenite) | |
| Asgari Yoğunluk (Alkol İle Yer Değiştirme Yöntemi) | 7.8 g/cm³ | |
Ürün Uygulamaları
Steel cut wires are produced from national standard bead wires and are widely applied in machinery, automotive, shipbuilding, steel structure, pipeline industries, and other manufacturing sectors for surface cleaning and strengthening of workpieces. During shot blasting, the cut wire shots are propelled at high speed by the blasting machine in a parabolic trajectory, effectively removing rust and oxide layers from the product surface while achieving the required finish and surface roughness. Among the available sizes, CW1.5mm is the most commonly used, with hardness typically exceeding 50HRC.
Due to their higher hardness, usually above 50HRC, steel cut wire shots can sometimes cause scuffing on softer materials, particularly those with hardness below 48HRC. For this reason, it is often recommended to mix steel cut wire shots with steel shots or steel grits of similar size for shot blasting. In practice, some customers also mix low-carbon steel shots with steel cut wire shots, which has proven to deliver excellent blasting results.